PP modified granulation
PPPellets：
| Main performance parameters | unit | Test Conditions | standard test | Black PP | Light grayPP | Flame retardantPP |
| Tensile Strength | Mpa | 50mm/min | GB/T 1040.2-2006 | 19.74 | 20.68 | 19 |
| Elongation at break | % | 50mm/min | GB/T 1040.2-2006 | 20.2 | 70.28 | 38 |
| Izod notched impact strength | kJ/m2 | Injection | GB/T 1843-2008 | 4.2 | 4.5 | 5 |
| Bending strength | Mpa | 10mm/min | GB/T 9341-2000 | 22.77 | 25.12 | 24 |
| Flexural modulus(MPa) | Mpa | 10mm/min | GB/T 9341-2000 | 759.11 | 910.49 | 870 |
| The melt flow rate | g/10min | 230℃/2.16kg | GB/T 3682-2000 | 18 | 27 | 20 |
| Application field | Plastic parts, motorcycle parts, packaging materials | |||||